No kā ir izgatavots penijs?

Pirmais santīms tika kalts Amerikas Savienotajās Valstīs 1787. gadā. Bendžamins Franklins, viens no Amerikas Savienoto Valstu dibinātājiem, ierosināja tā sākotnējo dizainu. Pirmā kaltā santīma sastāvs bija 100% tīrs varš. Tas turpinājās līdz 1800. gadu vidum, kad tika veiktas pirmās pensa sastāva izmaiņas.

The bronze penny was introduced in 1837, made of 95 percent copper and five percent zinc and tin. These pennies were minted for another 20 years before the next change was made. In 1857, the common penny received a further degradation in its copper content, and was made of 88 percent copper and 12 percent nickel. This gave the penny a lighter, almost white, hue.

In 1864, the penny returned to its previous bronze composition, of 95 percent copper and 5 percent zinc and tin. This continued until 1962, with the exception of one year. The 1943 penny was made of steel coated with zinc, due to a copper shortage. Because copper and nickel were sorely needed for making weapons for World War II, there wasn’t enough of the material to spare for minting pennies.

1943. gadā tika izkalti daži vara santīmi, un tie joprojām ir ļoti pieprasīti kolekcionāru priekšmeti to retuma dēļ. Mūsdienās ir zināmi tikai četrdesmit no 1943. Saskaņā ar Amerikas Savienoto Valstu monētu kaltuves datiem, tiek uzskatīts, ka šie vara santīmi ir izgatavoti nejauši, kad presē tika atstātas vairākas vara sagataves, sākot jauno tērauda peniju ražošanu.

Pēc 1962. gada santīma alvas saturs tika pilnībā noņemts, un cents tika kalts ar sastāvu, kurā bija 95 procenti vara un 5 procenti cinka. Tas palika standarts līdz 1982. gadam, kad sastāvs atkal tika mainīts. Šoreiz santīma vara saturs tika krasi samazināts. Jaunais penss sastāvēja no 97.5 procentiem cinka un 2.5 procentiem vara, kas pazīstams arī kā ar varu pārklāts cinks, un tāds tas ir arī šodien.